The first is to confirm and bake the battery material. Generally, the battery conductive agent needs to be baked at 120℃ for 8 hours. The PVDF powder should be baked at 80℃ for 8 hours. The cathode active material (LFP, NCM, etc.) depends on the state and process of incoming material whether it needs to be baked and dried. After drying, (wet process) Mixing the PVDF powder and NMP solvent to make ...
read more
-
The anode of lithium battery is composed of anode active materials, conductive agent, battery binder and dispersant. The conventional anode electrode system is a water mixing process (the solvent is deionized water), so the incoming material does not require drying. This process requires: Conductivity of deionized water ≤1us/cm. Workshop temperature ≤40℃, Humidity :≤25%RH. After confirmation of th...
read more
-
The cathode electrode coating is the cathode slurry extrusion coating or spraying on the cathode current collector aluminum foil, the density of one side is 20 to 40 mg/cm2. Coating oven temperature conventional 4-8 sections (or more), each section of baking temperature 95℃ ~ 120℃ according to the actual needs to adjust, to avoid baking cracking transverse cracks and solvent phenomenon, the speed ...
read more
-
Drying the battery cathode electrode after battery coating process, it is necessary to roll the coated battery electrode foil during the process time. The electrode rolling process is to compacting the coated electrode, at present there are hot pressing and cold pressing two processes of battery electrode rolling press. Battery electrode hot press compaction rate is higher than cold press, and the...
read more
-
Battery electrode winding is the separator, cathode sheet, anode sheet through the battery electrode winding machine into a single battery cells. TOB New Energy can provide the battery winding machine for 18650 lithium-ion cylindrical cell precision winding for 18650 production line. The principle of battery winding is to use the anode to cover the cathode, and then through the battery separator t...
read more
-
Lithium battery production process mainly includes battery cathode and anode slurry mixing, positive and negative electrode coating, roller pressing, electrode cutting, battery electrode making and die cutting, respectively corresponding to mixer, coating machine, roller press, slitting machine, electrode notching machine and electrode die cutting machine. The previous process of lithium battery -...
read more
-
After the electrode coating and drying, the peeling strength between the active material and the current collector foil is very low, and it needs to be rolled to enhance the bonding strength of the active material and the foil, to prevent peeling during immersion in electrolyte and battery use. At the same time, the roller pressing of the electrode can compress the volume of the cell, improve the ...
read more
-
Prussian Blue Cathode Materials for Aqueous Sodium-ion Batteries: Preparation and Electrochemical Performance Author：LI Yong. Prussian Blue Cathode Materials for Aqueous Sodium-ion Batteries: Preparation and Electrochemical Performance. Journal of Inorganic Materials[J], 2019, 34(4): 365-372 doi:10.15541/jim20180272 TOB New Energy can provide a full set of battery material and batte...
read more
-
Enhanced Lithium Storage Stability Mechanism of Ultra-high Nickel LiNi0.91Co0.06Al0.03O2@Ca3(PO4)2 Cathode Materials Author：ZHU Hezhen, WANG Xuanpeng, HAN Kang, YANG Chen, WAN Ruizhe, WU Liming, MAI Liqiang. Enhanced Lithium Storage Stability Mechanism of Ultra-high Nickel LiNi0.91Co0.06Al0.03O2@Ca3(PO4)2 Cathode Materials. Journal of Inorganic Materials, 2022, 37(9): 1030-1036...
read more
-
Cobalt-doped Hollow Carbon Framework as Sulfur Host for the Cathode of Lithium Sulfur Battery Author: JIN Gaoyao, HE Haichuan, WU Jie, ZHANG Mengyuan, LI Yajuan, LIU Younian. Cobalt-doped Hollow Carbon Framework as Sulfur Host for the Cathode of Lithium Sulfur Battery. Journal of Inorganic Materials[J], 2021, 36(2): 203-209 DOI:10.15541/jim20200161 TOB New Energy provides various battery...
read more
-
High-quality Fe4[Fe(CN)6]3 Nanocubes Preparation: As Cathode Material for Aqueous Sodium-ion Battery WANG Wu-Lian. High-quality Fe4[Fe(CN)6]3 Nanocubes: Synthesis and Electrochemical Performance as Cathode Material for Aqueous Sodium-ion Battery. Journal of Inorganic Materials[J], 2019, 34(12): 1301-1308 doi:10.15541/jim20190076 High-quality Fe4[Fe(CN)6]3 (HQ-FeHCF) nanocu...
read more
-
High-quality Fe4[Fe(CN)6]3 Nanocubes Preparation: As Cathode Material for Aqueous Sodium-ion Battery WANG Wu-Lian. High-quality Fe4[Fe(CN)6]3 Nanocubes: Synthesis and Electrochemical Performance as Cathode Material for Aqueous Sodium-ion Battery. Journal of Inorganic Materials[J], 2019, 34(12): 1301-1308 doi:10.15541/jim20190076 Part 2: Structure Characterization of Fe4[Fe...
read more
-
High-quality Fe4[Fe(CN)6]3 Nanocubes Preparation: As Cathode Material for Aqueous Sodium-ion Battery WANG Wu-Lian. High-quality Fe4[Fe(CN)6]3 Nanocubes: Synthesis and Electrochemical Performance as Cathode Material for Aqueous Sodium-ion Battery. Journal of Inorganic Materials[J], 2019, 34(12): 1301-1308 doi:10.15541/jim20190076 Electrochemical Performance Test of High-quality ...
read more
-
Cobalt-doped Hollow Carbon Framework as Sulfur Host for the Cathode of Lithium Sulfur Battery - Part 1 JIN Gaoyao, HE Haichuan, WU Jie, ZHANG Mengyuan, LI Yajuan, LIU Younian Hunan Provincial Key Laboratory of Micro & Nano Materials Interface Science, College of Chemistry and Chemical Engineering, Central South University, Changsha 410083, China Abstract Lithium-sulfur batteries are deemed to ...
read more
-
The battery slurry is a highly viscous solid-liquid two-phase suspension system, and to assess the stability of this system, the first step is to study its composition and its functional properties. Most of the lithium industry uses oil-based slurry, which is a mixture formed by mixing and dispersing active materials, binders, conductive agents, solvents, etc. in a certain ratio and order. Cathode...
read more
-
Battery electrode coating is a critical process in the manufacturing of batteries, as it affects the performance, efficiency, and quality of the final product. Electrode coating involves the application of a slurry onto a substrate, such as a metal foil or a current collector, to create a uniform and thin layer of active material, such as lithium cobalt oxide, graphite, or silicon, that can store ...
read more
-
The Preparation Method of Battery Cathode Slurry Wet Electrode Preparation Process A double planetary mixer was used as the cathode electrode slurry preparation equipment. First, prepare polyvinylidene fluoride (PVDF) glue. Use an ordinary mixing tank to pour a certain amount of solvent NMP (N-methylpyrrolidone) first, add the binder PVDF powder according to the designed solid content, and stir fo...
read more
-
Lithium-ion batteries are widely used in various fields due to their high energy density, long cycle life and environmental friendliness. The anode electrode slurry is one of the key components of lithium-ion batteries, which affects the performance and safety of the batteries. Therefore, it is important to understand the preparation process and precautions of the anode electrode slurry. The prepa...
read more
-
Lithium-ion batteries are widely used in various fields, such as electric vehicles, consumer electronics, energy storage and aerospace. The performance and quality of lithium-ion batteries depend on the electrode materials and their processing methods. One of the key processes in electrode manufacturing is calendering, which is the compression of the electrode slurry coated on the current collecto...
read more
-
Sb Doped O3 Type Na0.9Ni0.5Mn0.3Ti0.2O2 Cathode Material for Na-ion Battery KONG Guoqiang, LENG Mingzhe, ZHOU Zhanrong, XIA Chi, SHEN Xiaofang. Sb Doped O3 Type Na0.9Ni0.5Mn0.3Ti0.2O2 Cathode Material for Na-ion Battery[J]. Journal of Inorganic Materials, 2023, 38(6): 656-662. Abstract Cycle stability and specific capacity of cathode materials for sodium ion batteries play an important role i...
read more
中文
français
Deutsch
italiano
español
português
Nederlands
日本語
한국의
subscribe to us 